Low temperature hot corrosion effects on the low cycle fatigue (LCF) life and fracture morphology of a Udimet 720 alloy and the effectiveness of a protective coating in minimizing life degradation are reported. Strain controlled, continuous cycling (1 cpm) and 1 h hold (at maximum tensile strain) tests at 1350°F (732°C) in air revealed only small changes in life that could be attributed to creep during the 1 h hold. The presence of a corrosive salt environment, however, resulted in more than an order of magnitude degradation in life. In air and salt, the fracture was initially transgranular, but in salt it quickly changed to an intergranular mode, particularly at cyclic strains above 0.65 percent. These differences are attributed to reductions of 95 and 28 percent in the respective ductility and fatigue strength coefficients in the Coffin-Manson and Basquin relationships between cyclic strain and life. At cyclic strains ≤ ± 0.5 percent, a diffusion aluminide coating was protective in 1350°F (732° C) salt, with lives equivalent to those for the coated alloy in air; but at higher strains, coating failure occurred. Insignificant differences in fatigue life in air were noted for Udimet 720 and Udimet 710 alloys.
Skip Nav Destination
Article navigation
January 1984
Research Papers
Intermediate Temperature, Low-Cycle Fatigue Behavior of Coated and Uncoated Nickel Base Superalloys in Air and Corrosive Sulfate Environments
G. A. Whitlow,
G. A. Whitlow
Westinghouse Research and Development Center, Pittsburgh, Pa. 15235
Search for other works by this author on:
R. L. Johnson,
R. L. Johnson
Westinghouse Research and Development Center, Pittsburgh, Pa. 15235
Search for other works by this author on:
W. H. Pridemore,
W. H. Pridemore
Westinghouse Research and Development Center, Pittsburgh, Pa. 15235
Search for other works by this author on:
J. M. Allen
J. M. Allen
Westinghouse Combustion Turbine Systems Division, Concordville, Pa. 19331
Search for other works by this author on:
G. A. Whitlow
Westinghouse Research and Development Center, Pittsburgh, Pa. 15235
R. L. Johnson
Westinghouse Research and Development Center, Pittsburgh, Pa. 15235
W. H. Pridemore
Westinghouse Research and Development Center, Pittsburgh, Pa. 15235
J. M. Allen
Westinghouse Combustion Turbine Systems Division, Concordville, Pa. 19331
J. Eng. Mater. Technol. Jan 1984, 106(1): 43-49 (7 pages)
Published Online: January 1, 1984
Article history
Received:
April 25, 1983
Online:
September 23, 2009
Citation
Whitlow, G. A., Johnson, R. L., Pridemore, W. H., and Allen, J. M. (January 1, 1984). "Intermediate Temperature, Low-Cycle Fatigue Behavior of Coated and Uncoated Nickel Base Superalloys in Air and Corrosive Sulfate Environments." ASME. J. Eng. Mater. Technol. January 1984; 106(1): 43–49. https://doi.org/10.1115/1.3225675
Download citation file:
Get Email Alerts
Evaluation of Machine Learning Models for Predicting the Hot Deformation Flow Stress of Sintered Al–Zn–Mg Alloy
J. Eng. Mater. Technol (April 2025)
Blast Mitigation Using Monolithic Closed-Cell Aluminum Foam
J. Eng. Mater. Technol (April 2025)
Irradiation Damage Evolution Dependence on Misorientation Angle for Σ 5 Grain Boundary of Nb: An Atomistic Simulation-Based Study
J. Eng. Mater. Technol (July 2025)
Related Articles
Influence of an Aluminide Coating on the TMF Life of a Single Crystal Nickel-Base Superalloy
J. Eng. Gas Turbines Power (October,1999)
Aero Engine Test Experience With CMSX-4® Alloy Single-Crystal Turbine Blades
J. Eng. Gas Turbines Power (April,1996)
Development and Turbine Engine Performance of Three Advanced Rhenium Containing Superalloys for Single Crystal and Directionally Solidified Blades and Vanes
J. Eng. Gas Turbines Power (July,1998)
Improved Performance Rhenium Containing Single Crystal Alloy Turbine Blades Utilizing PPM Levels of the Highly Reactive Elements Lanthanum and Yttrium
J. Eng. Gas Turbines Power (January,1999)
Related Proceedings Papers
Related Chapters
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies
Effect of Hydrogen on Corrosion of Zircaloy-4 under Irradiation
Zirconium in the Nuclear Industry: 20th International Symposium
Advanced PWR Cladding Development through Extensive In-Reactor Testing
Zirconium in the Nuclear Industry: 20th International Symposium