Foreign object damage behavior of an oxide/oxide (N720/AS) ceramic matrix composite was determined at ambient temperature using impact velocities ranging from 100 m/s to 400 m/s by 1.59 mm diameter steel-ball projectiles. Two different support configurations of target specimens were used: fully supported and partially supported. The degree of post-impact strength degradation increased with increasing impact velocity and was greater in a partially supported configuration than in a fully supported one. For the fully supported configuration, frontal contact stress played a major role in generating composite damage, while for the partially supported case, both frontal contact and backside flexure stresses were the combined sources of damage generation. The oxide/oxide composite was able to survive high energy impacts without complete structural failure. The degree of relative post-impact strength degradation of the oxide/oxide composite was similar to that of an advanced SiC/SiC composite observed from a previous study, regardless of the type of specimen support. Like the SiC/SiC composite, impact-damage tolerance was greater in the oxide/oxide than in monolithic silicon nitride ceramics for impact velocities .
Foreign Object Damage in an Oxide/Oxide Composite at Ambient Temperature
- Views Icon Views
- Share Icon Share
- Search Site
Choi, S. R., Alexander, D. J., and Kowalik, R. W. (December 24, 2008). "Foreign Object Damage in an Oxide/Oxide Composite at Ambient Temperature." ASME. J. Eng. Gas Turbines Power. March 2009; 131(2): 021301. https://doi.org/10.1115/1.2969091
Download citation file: